DIVERSI MIŻURI BIEX TITTWOL IL-ĦAJJA TA' SERVIZZ TA' CASTABLES TAL-INSIRU TAL-BOILER

Il-castable refrattorju tal-bojler tas-sodda fluwidizzata li jiċċirkola hija parti importanti li taffettwa ċ-ċiklu tat-tħaddim tal-bojler. Il-grad refrattarju, is-saħħa termali, ir-rata ta 'jinxtorob, il-kwalità tat-tferrigħ, il-manutenzjoni u l-forn tal-castable jaffettwaw direttament is-saħħa u l-ħajja tal-ħajt tal-bojler. Taffettwa ċ-ċiklu tat-tħaddim tal-bojler, u fl-istess ħin, il-kwalità tal-preservazzjoni tas-sħana u l-protezzjoni barra l-korp tal-forn tirrestrinġi l-espansjoni tal-bojler, speċjalment fix-xitwa meta t-temperatura tkun inqas minn nieqes 5 gradi, minħabba l-espansjoni asinkronika uniformità, huwa faċli li tikkawża stress fil-ġonot tal-weldjatura tal-partijiet rilevanti tal-pipeline. L-għeluq tal-forn ċentralizzat u li jnixxi jnaqqas iċ-ċiklu tat-tħaddim, iżid in-numru ta 'fran u l-input ta' fran, jaffettwa t-tħaddim bla xkiel tal-unità tas-sistema, u jżid ir-riskju tal-operat. Permezz tal-problemi misjuba matul it-tħaddim attwali tal-bojler u waqt l-għeluq u l-manutenzjoni, il-castable kien parzjalment bil-ħsara waqt il-kostruzzjoni, u ma kien hemm l-ebda vojt ta 'espansjoni riżervat waqt il-kostruzzjoni u insulazzjoni esterna mhux xierqa kkawża differenzi kbar fit-temperatura bejn ġewwa u barra. Ir-raġunijiet ewlenin għall-ħsara huma xquq. Billi tiddiskuti l-mekkaniżmu materjali, tuża partijiet, u ssaħħaħ il-kontroll tal-link, huwa ttamat li jinkiseb l-iskop li tittejjeb il-ħajja tas-servizz.
Analiżi tas-Sitwazzjoni Kurrenti ta 'Circulating Fluidized Bed
Il-kapaċità tat-tagħbija tal-bojlers tal-impjant tal-enerġija tal-minjiera tal-faħam stess hija relattivament baxxa, li ħafna minnhom qed jiċċirkolaw bojlers tas-sodda fluwidizzata bi proprjetajiet ta 'utilizzazzjoni komprensivi li jużaw karburanti inferjuri, u l-kapaċità tal-evaporazzjoni hija l-aktar 75t/h u 130t/ h. Minħabba l-użu ta 'fjuwil inferjuri, il-valur kalorifiku huwa baxx, il-kontenut ta' rmied huwa għoli, iż-żennuna tal-gagazza tal-bojler, l-angolu tal-fjamma mitwi tal-forn, il-castable reżistenti għall-ilbies fir-riġlejn tal-kolonna tal-alimentatur tal-faħam u s-separatur taċ-ċiklun huma suxxettibbli għal xquq, xedd u kedd, Castable reżistenti għall-ilbies huwa l-fattur ewlieni li jirrestrinġi l-operat fit-tul tal-bojler; l-għażla ta 'protezzjoni esterna u materjali ta' insulazzjoni u l-kwalità tal-kostruzzjoni tal-bojler huma t-telf tas-sħana, u l-ġonta tal-welding fejn il-konċentrazzjoni tal-istress hija faċilment ikkawżata mit-tisħin tal-forn tal-post u l-waqgħa f'daqqa fit-temperatura ambjentali esterna. Fl-istess ħin, bir-rekwiżiti ta 'protezzjoni ambjentali dejjem aktar stretti, meta l-Ca/S=1.5-2.0 tal-bojler b'desulfurization tal-injezzjoni tal-kalċju fil-forn, l-effiċjenza tad-desulfurization tista' tilħaq {{8 }} fil-mija, ir-rata ta 'utilizzazzjoni tat-trab tal-ġebla tal-franka hija kważi d-doppju ta' dik tal-bojler tas-sodda fluwidizzata konvenzjonali, iżda l-input ta 'desulfurizer iżid l-ammont ta' materjal tas-sodda u materjal li jiċċirkola, u jżid l-ilbies ta 'castables tal-ħajt tal-forn. L-ilbies ta 'castables reżistenti għall-ilbies jesponi l-ħajt tal-film imkessaħ bl-ilma u l-pjanċa ta' protezzjoni ta 'barra. F'każijiet severi, il-pjanċa ta 'lqugħ hija maħruqa, deformata, maqsuma, u l-fittings tal-pajpijiet li jġorru l-pressjoni jnixxu minħabba s-saħħa mnaqqsa tal-ilbies, li tqassar ħafna l-perjodu ta' operazzjoni, iżid ir-rata tal-inċidenti, u taffettwa l-produzzjoni Sikura u żieda fil-materjal u input tax-xogħol.
Analiżi tal-prestazzjoni ta 'castables reżistenti għall-ilbies f'partijiet importanti tal-bojlers
The furnace wall of the low magnification circulating fluidized bed boiler adopts the tube-laying light furnace wall, the cyclone separator, the inclined flue, the furnace top and the tail flue are built with refractory castables, phosphate bricks and aluminum silicate insulation materials. High-strength composite refractory castables are poured into the lower part of the membrane-type water-cooled wall of the furnace. Different forms of refractory materials are selected and used according to the fluidization rate, flue gas flow rate, and refractory degree, so as to reduce construction and maintenance costs while ensuring service life and wear resistance. . The wear-resistant castable is made by mixing oxides and binders. The fluidized bed boiler furnace uses high-strength refractory castables with good fluidity. There are great differences in wear resistance, etc., which affect the boiler operation cycle. The refractory materials in the high temperature zone of the circulating fluidized bed boiler are mainly high-strength refractory castables. The main components are Al2O3+TiO2, and Portland cement is blended in a certain proportion. Due to different processes, the refractoriness, linear expansion rate, wear resistance There is a big difference in strength, which affects the service life of the boiler. The composition (quality parameter) of the alum clinker should be Al2O3>60 fil-mija , SiO2<20%, Fe2O3<3%; the concrete should be dried to remove moisture, and the basic refractory Do not dry when cemented with phosphoric acid. When acid and neutral refractories are cemented with phosphoric acid, immediately dry at 350℃<450℃<. (The phosphate solution is adjusted with 50% phosphoric acid and industrial aluminum hydroxide in a mass ratio of 7:1) According to the comparison of the physical properties of the castable, the phosphate refractory castable has high strength and hardness, and has a good linear expansion coefficient. To meet the requirements of use, it is fixed on the pressure furnace wall by 1Cr18Ni9Ti stainless steel nails, and has good adhesion with the furnace wall 20G membrane water cooling wall.
Il-fatturi ewlenin li jaffettwaw il-ħajja ta 'castables reżistenti għall-ilbies
1. L-influwenza tal-istruttura tal-bojler
Skont il-karatteristiċi strutturali tal-bojler, il-bojler tas-sodda fluwidizzata li jiċċirkola prinċipalment juża l-irmied maħruq fil-forn biex jitla 'bl-arja sħuna, u ċ-ċiklun fil-ħruġ tal-forn jipproduċi qtugħ u għarqa li jdur, u l-flussi tal-materjal tar-ritorn fil-forn permezz tal-arja tar-ritorn, it-temperatura tat-tliet partijiet b'temperatura ogħla tal-bojler waqt it-tħaddim normali huma: (1), tħaddim tal-forn: 900 grad (2), żbokk tal-forn: 892 grad ⑶, separatur taċ-ċiklun: 852 grad . Il-veloċità tad-duħħan hija: forn 5m/s, ħruġ tal-forn 5m/s, u separatur taċ-ċiklun 9.5m/s. Temperatura ogħla u veloċità tad-duħħan se jżidu l-ilbies ta 'castables reżistenti għall-ilbies, u trattament reżistenti għall-ilbies għandu jissaħħaħ.
2. L-effett tal-fjuwil
Il-fjuwil tal-bojler huwa l-prodotti sekondarji tal-gangue tal-ħasil tal-impjanti tal-preparazzjoni tal-faħam, ħama tal-faħam u faħam imħallat tal-ħasil, b'valur kalorifiku baxx u kontenut għoli ta 'rmied, li jikkawża xedd tal-castables reżistenti għall-ilbies u pajpijiet tal-ħajt imkessħa bl-ilma tal-forn waqt il-kombustjoni tat-togħlija. L-ilbies ta 'castables reżistenti għall-ilbies ta' separatur taċ-ċiklun u materjal ta 'ritorn huwa partikolarment serju. Il-ħsara lill-castables tista 'faċilment tikkawża li l-pjanċa tal-gwardja ta' barra tissaħħan direttament, tiġi deformata u maqsuma, u jseħħ il-fenomenu tat-tnixxija tad-duħħan u t-tnixxija tal-irmied. Jaffettwaw it-tħaddim normali tal-bojler, u l-ambjent tas-sit isir agħar.
3. L-impatt tal-kwalità tal-kostruzzjoni
Il-kwalità tal-kostruzzjoni hija l-fattur ewlieni li jaffettwa l-ħajja tas-servizz ta 'castables reżistenti għall-ilbies tal-bojler. Il-miżuri ta 'kostruzzjoni meħtieġa ma jittieħdux għall-kostruzzjoni staġjonali, il-proċess ta' kostruzzjoni ma jissodisfax ir-rekwiżiti standard, il-perjodu ta 'manutenzjoni huwa qasir, u l-forn ma jistax jinħema f'konformità stretta mal-kurva tal-forn mogħtija, li jirriżulta f' Il-forza tat-twaħħil u reżistenza għall-ilbies ta 'castables reżistenti għall-ilbies ma jistgħux jissodisfaw ir-rekwiżiti tad-disinn.
4. L-influwenza tal-varjazzjonijiet tat-tagħbija fuq il-castables waqt l-istadji tal-istartjar, l-għeluq u l-operat tal-bojler
Kontroll fqir tar-rata tat-tisħin u t-tkessiħ meta l-bojler ikun qed jissaħħan u jagħlaq biex jiksaħ jikkawża differenza kbira fit-temperatura bejn ġewwa u barra biex tifforma stress termali kbir. Il-falliment tat-tagħmir tal-għalf tal-faħam u l-bidla kbira fil-kwalità tal-faħam waqt it-tħaddim se jikkawżaw li t-temperatura tal-forn tvarja. Hemm varjazzjonijiet fit-temperatura tas-sodda ta '150 grad. L-ewwel, taffettwa l-parametri tal-fwar. It-tieni, il-volum tal-arja jeħtieġ li jiġi aġġustat fil-ħin. Il-varjazzjoni tal-proporzjon ta 'l-arja għall-faħam tikkawża t-tfixkil ta' l-istat tal-kombustjoni, li tikkawża li l-castable jitnaqqar għan-nar u jaffettwa l-użu ta 'castables reżistenti għall-ilbies. ħajja.